Abstract : Single crystals of CaAl4Si2O11 were synthesised at 1,500 degrees C and 14 GPa in a multi-anvil press, and the structure of the phase determined by single-crystal X-ray diffraction at room conditions. The structure-type is that of the "hexagonal barium ferrites". The space group of the average structure is P6(3)/mmc and the cell parameters are a = 5.4223(4) Angstrom, c = 12.7041(6) Angstrom, V = 323.28(5) Angstrom(3), with Z = 2, and its density is 3.905 g cm(-3) which is reasonable for a high-pressure alumino-silicate phase. The 22 oxygen and two calcium atoms within the unit-cell form an approximate hexagonal-close-packed array. Ten of the twelve octahedral interstices within this array that have only oxygen atoms for apices are filled with Si and/or Al. Ml octahedra share edges to form a spinel-like sheet of octahedra. The average bond length = 1.833 Angstrom suggests mixed occupancy by Si and Al. The Ml octahedral sheets are linked by shared corners to pairs of face-sharing M2 octahedra containing Al, with = 1.918 Angstrom. The remaining two cations of the unit-cell contents statistically occupy four tetrahedrally-coordi nated interstices, which occur as face-sharing pairs. The average bond length for these sites (1.742 Angstrom) suggests that they are occupied by Al, although Si occupancy cannot be excluded by the data. It is proposed that only one interstice of each pair is locally occupied, with the possibility of some short-range ordering of such occupancies. Complete long-range order leading to the acentric space group P6(3)mc is excluded by the data, as is the possibility of the average structure being comprised of merohedral (0 0 0 1) twins of P6(3)mc symmetry.
Type de document :
Article dans une revue
Physics and Chemistry of Minerals, Springer Verlag, 1999, 27 (1), pp.47--51. 〈10.1007/s002690050239〉
Liste complète des métadonnées

https://hal-upec-upem.archives-ouvertes.fr/hal-00693853
Contributeur : Admin Lge <>
Soumis le : jeudi 3 mai 2012 - 08:21:43
Dernière modification le : jeudi 3 mai 2012 - 08:21:51

Lien texte intégral

Identifiants

Collections

Citation

Laurent Gautron, Rj Angel, R Miletich. Structural characterisation of the high-pressure phase CaAl4Si2O11. Physics and Chemistry of Minerals, Springer Verlag, 1999, 27 (1), pp.47--51. 〈10.1007/s002690050239〉. 〈hal-00693853〉

Partager

Métriques

Consultations de la notice

89