Precipitation in original Duralumin A-U4G versus modern 2017A alloy

Magali Brunet

Résumé

Precipitation in Duralumin, a historic quaternary alloy of the type: Al–Cu–Mg–Si, was never fully studied nor observed by current electron microscopy techniques. This article presents the full characterization and comparison of two alloys: a Duralumin (A-U4G) from the 1950s collected on a vintage aircraft and its modern equivalent: a 2017A alloy. The as-received and peak-aging states were analysed with DSC, SAXS and TEM advanced techniques. It is shown that old Duralumin and modern 2017A present a similar nanoprecipitation in the as-received state and behave similarly upon artificial aging. As opposed to what has been reported in the past, three types of precipitates participating in hardening were found upon aging: θ’-Al2Cu, Q’(Q)-AlCuMgSi and Ω-Al2Cu.
Fichier principal
Vignette du fichier
Brunet_Materialia_2019_authors version (1).pdf (3.59 Mo) Télécharger le fichier
Origine : Fichiers produits par l'(les) auteur(s)
Loading...

Dates et versions

hal-02269041 , version 1 (22-08-2019)

Identifiants

Citer

Magali Brunet, Benoit Malard, Nicolas Ratel-Ramond, Christophe Deshayes, Sébastien Joulié, et al.. Precipitation in original Duralumin A-U4G versus modern 2017A alloy. Materialia, 2019, 8, pp.100429. ⟨10.1016/j.mtla.2019.100429⟩. ⟨hal-02269041⟩
220 Consultations
317 Téléchargements

Altmetric

Partager

Gmail Facebook X LinkedIn More